ORIGINAL ARTICLE
Year : 2015  |  Volume : 3  |  Issue : 1  |  Page : 16-22

Effect of desensitizers on retention of castings cemented to anatomically prepared teeth


Department of Prosthodontics and Crown and Bridge, Nair Hospital Dental College, Mumbai, Maharashtra, India

Correspondence Address:
Dr. Manish R Chauhan
A/304, Aabhas Complex, Behind Ramdevpeer Temple, Near Garden View Hospital, Tulinj Road, Nallasopara (East), Thane, Mumbai - 401 209
India
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/2347-4610.148515

Rights and Permissions

Context: The extensive use of desensitizing agents to control incidences of post-cementation sensitivity can variably affect the forces required for debonding of the prosthesis. The available literature offers inconsistent results and is generally carried out using a flat occlusal preparation. Aims: Evaluation of effect of desensitizing agents-nonpolymerizable (Systemp) and polymerizable (Clearfil SE Bond)-on retention of complete veneer castings luted to anatomically prepared teeth with zinc phosphate and glass ionomer cement (ZPC and GIC). Materials and Methods: Seventy maxillary second premolars were prepared conforming to the anatomic form to receive complete veneer castings. Two sets of dies were prepared; one for obtaining castings and second to permit mathematical calculation of the surface area. The specimens were divided into four experimental groups of 15 samples each and two control groups of 5 samples each. Two desensitizers and two luting cements were used. After cementation, the samples were tested at crosshead speed of 0.5 mm/min on universal testing machine (UTM) using a customized self-aligning device. Minimum load required to debond the specimens was recorded. Force value for each specimen was divided by its surface area to obtain the tensile bond strength. Results: Significant reduction in tensile bond strength was noted for all the experimental groups, irrespective of luting cement used. Conclusion: Systemp-glass ionomer group exhibited highest bond strength followed by Systemp-zinc phosphate, Clearfil SE Bond-glass ionomer and Clearfil SE Bond-zinc phosphate group.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed1950    
    Printed72    
    Emailed1    
    PDF Downloaded346    
    Comments [Add]    

Recommend this journal